以七水合硫酸锌(ZnSO4?7H2O)和六亚甲基四胺(HMT)为原料,采用化学浴沉积法合成了碱式硫酸锌(ZSH)微米片,并将其作为填料嵌入氟碳(FC)清漆中.采用傅里叶变换红外光谱仪、场发射扫描电镜、能谱仪和X射线衍射仪分析了ZSH微米片的健结构、形貌和组分.对比了不同ZSH的质量分数时在紫铜上所得FC–ZSH复合涂层的剖面结构、ZSH分布情况及腐蚀防护性能.结果表明,所得ZSH呈典型的六方片状晶...
The role of graphene loading on the corrosion-promotion activity of graphene/epoxy nanocomposite coatings
Graphene Polymer-matrix composites Coatings Corrosion
2023/6/21
It is still arguable whether graphene/polymer nanocomposite coating is corrosion inhibitors or promoters. This work aims to determine the "percolation threshold" for corrosion-promotion activity of th...
Partially dehydrated zinc hydroxide sulfate nanoplates reinforced coating for corrosion protection
Zinc hydroxide sulfate Dehydration Crystal phase transition Active barrier Synergistic effect
2023/6/21
In this work, partially dehydrated zinc hydroxide sulfate nanoplates are synthesized by facile chemical bath deposition together with subsequent heat dehydration. The nanoplates exhibit well-defined h...
通过开展Super304H及Inconel625合金的高温CO2腐蚀试验,并结合氧化增重法、扫描电镜观察及XRD分析,研究了两种耐热合金在750℃CO2掺杂SO2环境中的腐蚀行为。结果表明,两种合金在750℃CO2、750℃CO2+SO2环境中的腐蚀动力学均遵循抛物线规律,Inconel625抗腐蚀能力优于Super304H,具有较少的腐蚀增重;Super304H在750℃CO2腐蚀初期增重高于C...
超超临界锅炉在役S30432钢管高温腐蚀行为分析(图)
S30432 高温腐蚀 腐蚀产物层 腐蚀影响区
2023/3/30
通过微观组织分析、能谱成分分析和力学性能对泄露的S30432钢管高温腐蚀行为进行研究与分析。结果表明:管样发生爆破的原因是受到高温腐蚀的作用,管壁有效厚度减薄,同时爆破管组织发生老化,在介质的内压作用下,最终导致爆破泄漏。高温腐蚀层分为两层,外层为腐蚀产物层,内层为基体和孔洞、微裂纹相间的腐蚀影响区。与实验室模拟环境相比,在役S30432钢管受外壁结焦、烟气冲刷等因素影响,形成疏密相间的腐蚀产物,...
中国科学院金属研究所材料腐蚀与防护中心成果:高温高压水缝隙腐蚀研究(图)
高温高压 水环境 缝隙腐蚀
2022/6/24
中国科学院金属研究所材料腐蚀与防护中心核电材料腐蚀课题组研究方向
核电材料 腐蚀 课题组 研究方向
2022/5/17
中国科学院金属研究所材料腐蚀与防护中心成果:几种典型造币铜合金的单因素腐蚀性研究(图)
金属货币 铜合金 单因素 腐蚀性
2022/5/13
中国科学院金属研究所材料腐蚀与防护中心自然环境腐蚀研究部(国家野外站)(图)
材料环境 腐蚀规律 多相流 腐蚀机理
2022/5/12
中国科学院金属研究所材料腐蚀与防护中心自然环境腐蚀研究部大气腐蚀课题组(图)
大气环境 腐蚀规律 防护涂层技术
2022/5/12